Tempered Glass
The glass is derived from the float glass through the process to increase strength, by only technic with to make concrete is creates a layer of compressive strength on the glass surface to resist external forces, by give the heating with glass at higher temperatures weakness of little glass estimated 650°C – 700°C and make the glass surface to quickly cool, by the blow be cool at two side the mirrors, result of different the temperature between the skin with central texture of glass, will cause a layer of extrusion to the skin of two side glass plate, by it will be the central part like a sandwich and this layer will help to resist external forces resulting in a balanced action, shattering of glass to break into small grains like corn and a little sharp, Tempered Glass can not be drilled, grinded or otherwise processed, because the glass is broken.